Type: | CFC |
---|---|
Composition: | Carbon Fiber |
Carbon Content: | High-Carbon |
Grade: | Industrial Grade |
Forming Way: | Hot Press |
Crystal Morphology: | Compact Crystalline Graphite |
Customization: |
---|
Suppliers with verified business licenses
Material | CFC laminates |
Grade | FTCY-CFC |
Bulk Density(g/cm3) | 1.4~1.5 |
Carbon Content(%) | ≥98.5-99.9 |
Bending Strength(MPa) | 100~150 |
Tensile Strength(MPa) | 90~130 |
Flexural Strenth(MPa) | 100-200 |
Interlaminar Shear Strength(MPa) | ≥13 |
Compressive Strength(MPa) | 130~170 |
Tensile modulus(GPa) | 25~35 |
Coefficient of Linear Expansion(10-6/K) | 0.3~1.2 |
Resistivity(μΩ·k) | 30~43 |
Thermal Conductivity(W/m·k) | 10-30 |
Ash(PPM) | ≤65 |
Processing Temperature(ºC) | 2400 |
Material | CFC woven |
Grade | FTZC-C/C |
Bulk Density(g/cm3) | 1.5~1.8 |
Bending Strength(MPa) | 120~180 |
Tensile Strength(MPa) | 100~140 |
Interlaminar Shear Strength(MPa) | 10~15 |
Z-direction Compressive Strength(MPa) | 120~150 |
XY -direction Compressive Strength(MPa) | 180~250 |
Tensile Modulus(GPa) | 25~35 |
Coefficient of Linear Expansion(10-6/K) | 0.5~1.3 |
Resistivity(μΩ·k) | 15~40 |
Thermal Conductivity(W/m·k) | 30-50 |
Ash(PPM) | ≤100 |
Suppliers with verified business licenses